QIDI TPU-Aero

TPU-Aero is a medium-hard, reactive foaming flexible material developed specifically for FFF printing technology. By controlling the printing temperature, different foaming ratios can be achieved, thereby achieving different weight and hardness effects. Combined with excellent elasticity, wear resistance and lightweight properties, it can be used in sports equipment, industrial parts, aerospace prototypes and creative design.

Lightweight and excellent interlayer adhesion

TPU-Aero is more than 50% lighter than traditional TPU materials, has excellent interlayer adhesion, and the weight of the material can be controlled by adjusting the printing temperature. It is particularly suitable for weight-sensitive application scenarios such as sports equipment, aerospace, etc.

Adjustable weight and hardness

By adjusting the temperature, flow ratio or filling density, the hardness can be precisely controlled from 85A to 65A to achieve interesting different printing effects.

High resilience, high toughness

TPU-Aero has excellent deformation recovery ability, which is suitable for parts that need to be deformed repeatedly. It has strong tear and impact resistance and is not easy to break under extreme stress.

Matte Finish, Fabric Texture

Premium fabric-like texture meets engineering-grade performance,Stimulate your creative imagination

Low water absorption

It can maintain stable performance in water or humid environment and will not expand/deform due to water absorption

Compatibility

	Recommended	Not Recommended
Multi-color printing system	/	QIDI BOX, AMS, and other multi-color printing systems that require feeding through PTFE tubes
Spport Filament	PLA Basic	/
Build Plate	QIDI Cool Plate pro, QIDI PEI Plate and Smooth Plate(Spray alcohol to help remove print parts), HF Plate, PC Plate	/
Nozzle	Brass/Copper plated Nozzle(0.4 / 0.6mm ) Hardened Steel Nozzle ( 0.4 / 0.6mm ) Bimetal Nozzle ( 0.4 / 0.6mm )	Brass/Copper plated Nozzle(0.8 mm) Hardened Steel Nozzle (0.8 mm) Bimetal Nozzle (0.8 mm)
Glue	Glue Stick	/

Recommended Printing Settings
Drying Settings (Blast Drying Oven)	70-80 °C，4-6 h
Printing and Keeping Container's Humidity	< 15% RH (Sealed, with Desiccant)
Nozzle Temperature	230-270 °C
Bed Temperature (with Glue)	30-45 °C
Printing Speed	30-50 mm/s

Physical Properties
Density	0.74 g/cm³
Water absorption	1.09 %
Vicat softening temperature	70.4°C
Melt index	8 g/10min(190°C,2.16kg)

Mechanical Properties
Tensile strength(X-Y)	4.23±0.04 MPa
Tensile breaking strength (X-Y)	6.81±0.11 MPa
elongation at break (X-Y)	576.27±8.48 %

Specimens printed under the following conditions: print temperature 250°C,Flow ratio 0.68,Nozzle size 0.4mm，Bed temp 45°C, Print speed 60mm/s, Infill 100%, Infill angle ±45°

Downloads

Filament TDS

Filament MSDS

Printing Tips

TPU materials are prone to moisture absorption when exposed to air. It is recommended to put TPU-Aero filaments in a drying oven (humidity controlled below 15%) immediately after opening the vacuum foil packaging. Unused filaments should be resealed in the original foil packaging.
For TPU-Aero filaments that are exposed to air for a long time, it is recommended to put the filaments in a 70-80°C oven for 4-6 hours before printing to avoid problems such as bubbles, holes or drawing caused by moisture.
Due to the continuous expansion of the foaming material in the hot end cavity, leakage is inevitable during the stroke movement. Even adjusting the retraction distance and speed cannot improve this situation. It is recommended to disable the retraction function in the slicing software, print only one model at a time, or use the piece-by-piece printing function, and turn on the option to avoid crossing the outer wall to reduce drawing and leakage caused by long-distance idling and jumping.
Some of PEI textured or PEI film build plates may exhibit excessive adhesion to TPU materials, making printed parts difficult to remove. It is recommended to use alcohol to remove the parts.

For more details please refer to: Filament Guide on WIKI.

Vacuum Aluminum Foil Packaging

According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant.

Product Size

QIDI TECH TPU-Aero filament 1.75mmWorks perfectly with most FDM 3Dprinters on the market.

flash sale-2

Q1-Pro/X-Max 3/X-Plus 3/X-Smart 3 Hardened steel nozzle (2pcs)

ABS-GF25 Filament

PA12-CF Filament

Q2 Dual-sided smooth Plate

TPU-Aero Filament

Q2 Bimetal hot end